Boris, Are you using DC, reverse polarity? It does not take much gas flow for ferrous metals, unless there is a fan blowing on the weld. I have heard of people trying to be too comfortable, and blowing away the gas envelope.
Boris, Are you using DC, reverse polarity? It does not take much gas flow for ferrous metals, unless there is a fan blowing on the weld. I have heard of people trying to be too comfortable, and blowing away the gas envelope.
I also remembered, do you have your tungsten ground to a point?