You really don't want a core that's going to retain magnetism, which
4130 will. No matter how easy it is to get, it's not the stuff for the job. There's special steels for this purpose, for prototype purposes you might try cast iron or nodular iron. Both are very easy to machine. What's the hollow going to get you? Room for a return spring?Stan