What problems, if any, arise when welding hardened steel by TIG?
Josh
welding hardened steel
Jul 23, 2003
2 Replies
Most relevant reply
In message , JD Fowler writes Shrinkage cracking.Would advise some preheat to slow the cooling rate through the critical range 100deg.c-room temp.
Read the full reply
I'll add that I've had good luck using 312 or 309 stainless filler.
Ted
In message , JD Fowler writes
Shrinkage cracking.Would advise some preheat to slow the cooling rate through the critical range 100deg.c-room temp.